Polarizer having protection films in two sides and optical device comprising the same

ABSTRACT

A double-sided polarizer includes a polarizing film, a first adhesive layer formed on one surface of the polarizing film, a second adhesive layer formed on the other surface of the polarizing film, a first transparent film formed on the first adhesive layer, and a second transparent film formed on the second adhesive layer, wherein the first adhesive layer and the second adhesive layer are formed of an active energy line-curable adhesive and the first adhesive layer is 0.1 μm to 3 μm thick, and there is also provided an optical device including the double-sided polarizer.

TECHNICAL FIELD

The present invention relates to a double-sided polarizer and an opticaldevice including the same, and more particularly, to a double-sidedpolarizer having adhesive layers on both sides thereof which are onlycurable by irradiating light thereon once, to simplify the manufacturingprocess thereof, and has been developed such that an adhesive layer on anon-irradiated surface has superior adhesive force, and an opticaldevice including the same.

BACKGROUND ART

A polarizer is a film able to convert natural light into polarized lighthaving a specific vibration direction, and is employed in variousdisplay devices, such as liquid crystal displays, and organic lightemitting devices.

The polarizer includes a polarizing film made of a polyvinyl alcohol(PVA) resin dyed with dichroic dye or iodine, and a protective filmstacked on one surface or both surfaces of the polarizing film with anadhesive interposed therebetween. Until recent years, a triacetylcellulose (TAC) film has been widely used as a protective film. However,the TAC film has a drawback in that it may be deformed in a hightemperature and high humidity environment. Therefore, in recent years,protective films made of various materials capable of replacing the TACfilm have been developed, and for example, the use of polyethyleneterephthalate (PET), a cycloolefin polymer (COP), and an acrylic film,alone or mixtures thereof, has been proposed.

Meanwhile, examples of adhesives that may be used for attaching thepolarizing film and the protective film to each other include an acrylicadhesive, a dry laminated adhesive prepared by mixing a urethane resinsolution and a polyisocyanate resin solution, a styrene/butadiene/rubberadhesive, an epoxy adhesive, a polyvinyl alcohol adhesive, an urethaneadhesive, an adhesive containing a compound having a polyester ionomertype urethane resin and a glycidyl group, a thermosetting adhesive, orthe like, while water-based adhesives made of an aqueous solution ofpolyvinyl alcohol resin may chiefly be used.

However, in the case of the water-based adhesives, when an acrylic filmor COP film is used as the protective film instead of the TAC film, theadhesive force of the protective film is weak and thus the protectivefilm has a drawback in that use thereof is limited according to thematerial of the protective film. Also, in the case of the water-basedadhesives, in addition to adhesive failure due to the material, when theprotective films applied to both surfaces of a PVA polarizing film aremade of different materials, curling of the polarizer may occur in thecourse of a drying process of the water-based adhesives and a loweringof initial optical properties may be caused. As an alternative to solvethese drawbacks, a photo-curable non-water-based adhesive has beenproposed.

However, since the photo-curable non-water-based adhesives generallyhave a high viscosity, a final adhesive layer is so thick that when thepolarizer is manufactured by using the photo-curable non-water-basedadhesives, failure, such as curling in the TD and MD directions mayeasily occur.

Also, in the case of a double-sided polarizer with protective filmsattached to both surfaces of a polarizing film, since the adhesivelayers formed on both surfaces of the polarizing film should be cured,respectively, light irradiation should be performed twice, which makesthe process complicated. While the adhesive layer may be cured byirradiating light thereonto once, the degrees of curing of the adhesivelayers are not equal due to a difference between amounts of lightarriving at the light irradiation surface and the light non-irradiationsurface, and thus the adhesive force of the light non-irradiationsurface is low. Thus, the low adhesive force of the adhesive layerdeteriorates the durability of the polarizer to thus lower the opticalproperties of the polarizer.

DISCLOSURE Technical Problem

An aspect of the present invention provides a double-sided polarizerhaving adhesive layers on both sides thereof curable by only irradiatinglight thereonto once, to simplify the manufacturing process and has beendeveloped such that an adhesive layer on a non-irradiated surface hassuperior adhesive force, and an optical device including the same.

Technical Solution

According to an aspect of the present invention, there is provided adouble-sided polarizer including: a polarizing film; a first adhesivelayer formed on one surface of the polarizing film; a second adhesivelayer formed on the other surface of the polarizing film; a firsttransparent film formed on the first adhesive layer; and a secondtransparent film formed on the second adhesive layer, wherein the firstadhesive layer and the second adhesive layer are formed of an activeenergy line-curable adhesive and the first adhesive layer is 0.1 μm to 3μm thick.

The second adhesive layer may be preferably 0.1 μm to 10 μm thick. Thedouble-sided polarizer of the present invention may be manufactured bysimultaneously curing the first adhesive layer and the second adhesivelayer by irradiating an active energy line once, and the irradiating ofthe active energy line may be preferably performed through an activeenergy source positioned in the direction of the transparent film formedon the second adhesive layer.

Meanwhile, the first adhesive layer and the second adhesive layer may bepreferably formed of a cationic adhesive, which may include: (1) 5 wt %to 90 wt % of an epoxy compound having at least two epoxy groups in amolecule; (2) 5 wt % to 90 wt % of an oxetane compound having at leastone oxetanyl group in a molecule; and (3) 0.5 wt % to 20 wt % of acationic photo-polymerization initiator.

The double-sided polarizer may further include a primer layer at leastbetween the first adhesive layer and the first transparent film orbetween the second adhesive layer and the second transparent film, andthe primer layer may be preferably formed of a primer compositionincluding part to weight to 50 parts by weight of a urethane polymer,0.1 part by weight to 10 parts by weight of water-dispersed fineparticles, and the balance of water.

According to another aspect of the present invention, there is providedan optical device including a double-sided polarizer having the aboveconfiguration.

Advantageous Effects

According to the double-sided polarizer of the present invention, sincethe adhesive layer of an active energy line-non irradiated surface isformed to have a thickness within the range of 0.1 μm to 3 μm, theadhesive layers on both surfaces of the polarizer can be formed at thesame time by irradiating an active energy line once, thereby simplifyingthe manufacturing process.

Also, the double-sided polarizer of the present invention has superioradhesive force between the polarizer and the transparent film, superiordurability and water resistance, and superior optical property even inharsh environment.

BEST MODE

Hereinafter, the present invention will be described in more detail.

The present inventors have performed a large amount of research todevelop a double-sided polarizer having superior durability, heatresistance, and optical property, and as a result of the research, havedeveloped a double-sided polarizer of the present inventioncharacterized by forming an adhesive layer by using an active energyline-curable adhesive and at the same time forming the adhesive layer tohave a thickness within a specific range.

More specifically, the present invention relates to a double-sidedpolarizer including: a polarizing film; a first adhesive layer formed onone surface of the polarizing film; a second adhesive layer formed onthe other surface of the polarizing film; a first transparent filmformed on the first adhesive layer; and a second transparent film formedon the second adhesive layer, wherein the first adhesive layer and thesecond adhesive layer are formed of an active energy line-curableadhesive and the first adhesive layer is 0.1 μm to 3 μm thick.

In the present description, a double-sided polarizer means a polarizerincluding protective films attached to both surfaces of a polarizingfilm, and is discriminated from a single-sided polarizer.

In related art double-sided polarizers, a first adhesive layer and asecond adhesive layer are generally formed to have the same thickness,for example, a thickness ranging from 5 μm to 10 μm. However, in thecase of the related art double-sided polarizers having the foregoingadhesive thickness range, to obtain a sufficient adhesive force, lightshould be irradiated onto each of the first adhesive layer and thesecond adhesive layer for curing of the first adhesive layer and thesecond adhesive layer. This is because one light irradiation allows oneadhesive layer facing the light irradiation direction to securesufficient adhesive force, but the other adhesive layer not facing thelight irradiation direction to secure insufficient adhesive force. Thus,the related art doubled-sided polarizers have a drawback in that themanufacturing process is complicated.

However, as a result of the present inventors' studies, it wassurprisingly indicated that when an adhesive layer (for the convenienceof description, referred to as “first adhesive layer”) formed on anopposite side of an active energy line to an irradiation direction isformed to have a thickness ranging from 0.1 μm to 3 μm, only oneirradiation secured superior adhesive force in both adhesive layers onboth surfaces of a polarizing film. Table 1 below shows measurementresults of delamination force according to the thickness of the firstadhesive layer formed on an active energy line non-irradiated surface.

TABLE 1 Delamination force of first Thickness of first adhesive layeradhesive layer [N] >1 μm  2.5 1 μm 2.5 3 μm 2.5 5 μm 1.5 7 μm 0.5 10 μm 0.2

As shown in table 1 above, when the thickness of the first adhesivelayer exceeds 3 μm, the delamination force of the adhesive force isremarkably lowered. Thus, in the case that the delamination force of theadhesive layer is lowered, the polarizing film and the transparent filmmay be easily delaminated to thus have a bad influence on the durabilityand optical properties of the polarizer.

Meanwhile, it was proven that an adhesive layer (for the convenience ofdescription, hereinafter referred to as a “second adhesive layer”)formed on a side directly facing the irradiation direction of the activeenergy line did not show a difference in adhesive force according to thethickness thereof. If the thickness of the second adhesive layer is toothick, curling of a final product, i.e., a polarizer may occur. Thus, itis preferable that the second adhesive layer be formed as thinly aspossible. For example, in the present invention, the second adhesivelayer may be formed to be 0.1 μm to 10 μm thick, preferably 0.1 μm to 7μm thick, and more preferably, 0.1 μm to 5 μm thick.

The double-sided polarizer of the present invention configured as abovemay be manufactured by simultaneously curing the first adhesive layerand the second adhesive layer by irradiating an active energy line once,and the irradiating of the active energy line may be preferablyperformed through an active energy source positioned in the direction ofthe transparent film formed on the second adhesive layer. At this time,examples of the active energy source may include ultraviolet light, anelectron beam, microwaves, infrared light (IR), X-ray, a gamma-ray, anda particle beam, such as an alpha-particle beam, a proton beam, or aneutron beam, and ultraviolet light or an electron beam may typically beused.

In the present invention, it is preferable that the first adhesive layerand the second adhesive layer are formed of an active energyline-curable adhesive, cured by an active energy line. To form thethickness of the adhesive layer thinly as above, it is preferable thatthe active energy line-curable adhesive has a viscosity ranging from 15cP to 50 cP. In consideration of durability, thermal impact, or thelike, it is preferable that the active energy line-curable adhesive hasa glass transition temperature of not less than 90° C.

More preferably, the first adhesive layer and the second adhesive layermay be formed of a cationic adhesive. Herein, a cationic adhesive meansan adhesive of which a main component is a compound cured by a cationicpolymerization reaction.

For example, the cationic adhesive include: (1) 5 wt % to 90 wt % ofepoxy compound having at least two epoxy groups in a molecule; (2) 5 wt% to 90 wt % of oxetane compound having at least one oxetanyl group in amolecule; and (3) 0.5 wt % to 20 wt % of cationic photo-polymerizationinitiator.

The kinds of epoxy compound of (1) are not particularly limited if epoxycompounds have at least two epoxy groups in a molecule. For example,epoxy resins well known in the art, such as aromatic epoxy resins,alicyclic epoxy resins, or aliphatic epoxy resins alone or combinationsthereof may be used.

The aromatic epoxy means an epoxy including an aromatic group in amolecule, and may include, for example, a bisphenol type epoxy resin,such as a bisphenol A-type epoxy, a bisphenol F-type epoxy, a bisphenolS-type epoxy, or a brominated bisphenol type epoxy; a novolac type epoxyresin, such as a phenol novolac type epoxy resin and a cresol novolactype epoxy resin; a cresol epoxy, resorcinol glycidyl ether, and thelike.

The alicyclic epoxy means a compound of which an epoxy group is formedbetween two neighboring carbon atoms constituting an alicyclic ring, andmay include, for example, dicyclopentadien dioxide, limonene dioxide,4-vinylcyclohexene dioxide, 2,4-epoxycyclohexylmethyl3,4-epoxycyclohexane carboxylate, diclopentadien dioxide,bis(3,4-epoxycyclohexylmethyl)adipate, and the like.

The alicyclic epoxy may include a polyglycidyl ether of alicyclicpolyalcohol, an alkylene oxide-added polyglycidyl ether of alicyclicpolyalcohol, and the like.

The alicyclic polyalcohol may include, for example, alicyclicpolyalcohols having 2-20 carbon atoms. More specifically, the alicyclicpolyalcohol may include aliphatic diols, such as ethylene glycol,1,2-propanediol, 1,3-propanediol, 2-methyl-1,3-propanediol,2-butyl-2-ethyl-1,3-propanediol, 1,4-butanediol, neopentyl glycol,3-methyl-2,4-pentanediol, 2,4-pentanediol, 1,5-pentanediol,3-methyl-1,5-pentanediol, 2-methyl-2,4-pentane diol,2,4-diethyl-1,5-pentanediol, 1,6-hexanediol, 1,7-heptanediol,3,5-heptanediol, 1,8-octane diol, 2-methyl-1,8-octanediol,1,9-nonanediol, 1,10-decanediol; alicyclic diols, such ascyclohexanedimethanol, cyclohexanediol, hydrogenated bisphenol A,hydrogenated bisphenol F; and three or more-valent polyols, such astrimethylolethane, trimethylolpropane, hexitols, pentitols, glycerin,polyglycerin, pentaerythritol, dipentaerythritol, tetramethylol propane.

More specifically, the alkylene oxide may include, for example, ethyleneoxide, propylene oxide, butylene oxide, and the like.

Meanwhile, it is more preferable to use a combination of a first epoxycompound including an epoxidized aliphatic ring group, i.e., at leastone alicyclic epoxy ring, and a second epoxy compound including one ormore glycidyl ether group as the epoxy compound, but the presentinvention is not limited thereto.

By using the combination of the first epoxy compound and the secondepoxy compound, an adhesive for a polarizer with enhanced thermal impactproperties may be prepared. At this time, the first epoxy compound andthe second epoxy compound may be mixed preferably in a weight ratio of1:1 to 3:1, more preferably 1:1 to 2:1, most preferably 1:1. When theweight ratio of the first epoxy compound and the second epoxy compoundsatisfies the above range, the most preferable physical properties maybe obtained in regard to glass transition temperature, adhesive forceand viscosity. In the present invention, the first epoxy compound andthe second epoxy compound may be included by, for example 20-60 parts byweight with respect to 100 parts by weight of the overall adhesivecomposition.

The first epoxy compound may be at least one selected from the groupconsisting of, for example,3,4-epoxycyclohexylmethyl-3,4′-epoxycyclohexanecarboxylate,bis(3,4-epoxycyclohexylmethyl)adipate dicyclopentadiene dioxide,limonene dioxide, and 4-vinylcyclohexene dioxide. The first epoxycompound is used for elevating glass transition temperature (Tg), andproviding the adhesive layer with hardness, and may be most preferably3,4-epoxycyclohexylmethyl-3,4′-epoxycyclohexanecarboxylate.

The second epoxy compound is not particularly limited if it includes oneor more glycidyl ether group, and may be one or more selected from thegroup consisting of, for example, 1,4-cyclohexanedimethanol diglycidylether, novolac epoxy, bisphenol A-type epoxy, bisphenol F-type epoxy,brominated bisphenol type epoxy 1,6-hexanediol diglycidyl ether,trimethylolpropane triglycidyl ether, n-butyl glycidyl ether, aliphaticglycidyl ether (C12-C14), 2-ethylhexyl glycidyl ether, phenyl glycidylether, o-cresyl diglycidyl ether, and nonyl phenyl glycidyl ether. Thesecond epoxy compound is used for providing the adhesive with softnessand enhancing the adhesive force, more preferably includes an aliphaticring, and most preferably, may be 1,4-cyclohexanedimethanol diglycidylether.

Next, the oxetane compound of (2) is not particularly limited if it hasat least one oxetanyl group in a molecule, and may be an oxetanecompound well known in the art. Examples of the oxetane compound mayinclude 3-ethyl-3-[(3-ethyl-oxetane-3-yl)methoxy methyl]oxetane,1,4-bis[(3-ethyl oxetane-3-yl)methoxy methyl]benzene, 1,4-bis[(3-ethyloxetane-3-yl)methoxy]benzene,1,3-bis[(3-ethyl-oxetane-3-yl)methoxy]benzene,1,2-bis[(3-ethyl-oxetane-3-yl)methoxy]benzene, 4,4′-bis[(3-ethyloxetane-3-yl)methoxy]biphenyl,2,2′-bis[(3-ethyl-oxetane-3-yl)methoxy]biphenyl,3,3′,5,5′-tetramethyl-4,4′-bis[(3-ethyl oxetane-3-yl)methoxy]biphenyl,2,7-bis[(3-ethyl-oxetane-3-yl)methoxy]naphthalene, bis[4-{(3-ethyloxetane-3-yl)methoxy}phenyl]methane, bis[2-{(3-ethyloxetane-3-yl)methoxy}phenyl]methane,2,2-bis[4-{(3-ethyl-oxetane-3-yl)methoxy}phenyl]propane, etherifiedmodified compound by 3-chloro-methyl-3-ethyl oxetane of novolac-typephenol-formaldehy, 3(4),8(9)-bis[(3-ethyl oxetane-3-yl)methoxymethyl]-tricyclo-[5.2.1.0 2,6]decane, 2,3-bis[(3-ethyloxetane-3-yl)methoxy methyl]norbornane,1,1,1-tris[(3-ethyl-oxetane3-1)methoxy methyl]propane,1-butoxy-2,2-bis[(3-ethyl oxetane-3-yl)methoxy methyl]butane,1,2-bis[{2-(3-ethyl oxetane-3-yl)methoxy}ethylthio]ethane,bis[{4-(3-ethyl oxetane-3-yl)methylthio}phenyl]sulfide,1,6-bis[(3-ethyl-oxetane-3-yl)methoxy]-2,2,3,3,4,4,5,5-octa-fluoro-hexane,and the like. Meanwhile, the amount of the oxetane compound ispreferably 5 parts by weight to 90 parts by weight, more preferably 10parts by weight to 90 parts by weight.

Next, the cationic photo-polymerization initiator of (3) is a compoundproducing a cation species or Louis acid by irradiation of the activeenergy line, and may include, but is not limited to, for example, oniumsalts, such as an aromatic diazonium salt, an aromatic iodine aluminumsalt, or an aromatic sulfonium salt, iron-arene complexes, and the like.Meanwhile, the amount of the cationic photo-polymerization initiator is0.5 parts by weight to 20 parts by weight with respect to 100 parts byweight of the overall adhesive composition, preferably 0.5 parts byweight to 15 parts by weight, and more preferably 0.5 parts by weight to10 parts by weight.

The cationic adhesive composition of the present invention may furtherinclude a vinyl compound together with the foregoing components, ifnecessary. If a vinyl compound is added, low viscosity may bemaintained, and a lowering phenomenon in glass transition temperature ofthe adhesive layer after curing may be decreased.

Examples of the vinyl compound may be hydroxy-C1-6 alkyl vinyl etherand/or vinyl acetate, and the hydroxy-C1-6 alkyl vinyl ether may be atleast one selected from the group consisting of hydroxyethyl vinylether, hydroxybutyl vinyl ether, 1,4-cyclohexane dimethanol vinylether,4-(hydroxymethyl)cyclohexyl methyl vinyl ether, ethylene glycol vinylether, diethylene glycol monovinylether. The vinyl compound may becontained in a weight ratio of 0.1 parts by weight 10 parts by weight or0.1 parts by weight to 5 parts by weight with respect to 100 parts byweight of the overall adhesive composition.

The cationic adhesive composition of the present invention may furtherinclude a silane coupling agent if necessary together with the foregoingcomponents. The silane coupling agent may lower a surface energy of theadhesive to enhance wettability of the adhesive.

It is more preferable that the silane coupling agent includes cationicpolymerization functional groups, such as epoxy groups, vinyl groups,and radical groups. The present inventors have found that the use of thesilane coupling agent including the cationic polymerization functionalgroups may improve the wettability of the adhesive without lowering theglass transition temperature, unlike the case of not using the silanecoupling agent. The reason is that the cationic polymerizationfunctional groups of the silane coupling agent react with silane groupsof the adhesive composition to form cross-links, thus decreasing thelowering phenomenon in glass transition temperature of the adhesivelayer after curing.

The silane coupling agent that is usable in the present invention maybe, but limited to, for example, a silane coupling agent expressed byformula 1:

Si(R₁)_(n)(R₂)_(4-n)  [Formula 1]

where R1 is a cationic polymerization functional group that is bonded toSi atom and includes a cyclic ether group or a vinyloxy group, R2 ishydrogen, a hydroxy group or an alkoxy group bonded to an Si atom, and nis an integer between 1 and 4.

Concrete examples of the silane coupling agent satisfying Formula 1 mayinclude, but are not limited to, 2-(3,4-epoxycyclohexyl)ethyl trimethoxysilane, 3-glycildoxypropyl trimethoxy silane, glycidoxypropylmethyldiethoxy silane, glycidoxypropyl triethoxy silane, vinyltrimethoxysilane or vinylethoxy silane.

Also, the silane coupling agent usable in the present invention mayinclude an oligomer type silane compound including cationicpolymerization function groups introduced into a molecule of siloxaneoligomer. At this time, the siloxane oligomer may be a low molecularsilicon resin of which a molecular-chain end is blocked by analkoxysilyl group.

At this time, the cationic adhesive composition may be contained in aweight ratio of 0.1 parts by weight 10 parts by weight or 0.1 parts byweight to 5 parts by weight with respect to 100 parts by weight of theoverall adhesive composition. The adhesive layer may exhibit a propersurface energy and an adhesivity in the above range.

Meanwhile, the cationic adhesive composition of the present inventionmay further include a radical polymerization monomer if necessary.Compounds having a radical reactive function group may be used for theradical polymerization monomer without any limitation, and may include,for example, (meth)acrylates having one or more (meth)acryloyl group,(meth)acrylic amides, maleimides, (meth)acrylic acid, maleic acid,itaconic acid, (meth)acryl aldehyde, (meth)acryloyl morpholine,N-vinyl-2-pyrrolidone, triallylisocyanulate, and the like.

Concrete examples of (meth)acrylates having one (meth)acryloyl group ina molecule may include methyl(meth)acrylate, ethyl(meth)acrylate,propyl(meth)acrylate, isopropyl(meth)acrylate, butyl(meth)acrylate,isobutyl(meth)acrylate, 2-ethylhexyl(meta)acrylate, octyl(meth)acrylate,isooctyl(meth)acrylate, lauryl(meth)acrylate, stearyl(meth)acrylate,2-hydroxyethyl(meth)acrylate, 2-hydroxy-propyl(meth)acrylate,4-hydroxybutyl(meth)acrylate, cyclohexyl(meth)acrylate,isobornile(meth)acrylate, 1,4-cyclohexane dimethylolmono(meth)acrylate,dicyclopentanyl(meth)acrylate, dicyclopentenyl(meth)acrylate,dicyclopentenyloxyethyl(meth)acrylate, benzyl(meth)acrylate,(meth)acrylate of phenol alkylene oxide adduct, (meth)acrylate ofp-kumil phenol alkylene oxide adduct, (meth)acrylate of o-phenyl-phenolalkylene oxide adduct, (meth)acrylate of nonyl phenol alkylene oxideadduct, 2-methoxy-ethyl(meth)acrylate, ethoxy ethoxyethyl(meth)acrylate,(meth)acrylate of 2-ethylhexyl alcohol alkylene oxide adduct, ethyleneglycol mono(meth)acrylate, propylene glycol mono(meth)acrylate, pentanediol mono(meth)acrylate, hexanediol mono(meth)acrylate, diethyleneglycol mono(meth)acrylate, triethylene glycol mono(meth)acrylate,tetraethylene glycol mono(meth)acrylate, polyethylene glycolmono(meth)acrylate, dipropylene glycol mono(meth)acrylate, tripropyleneglycol mono(meth)acrylate, polypropylene glycol mono(meth)acrylate,2-hydroxy-3-phenoxy-propyl(meth)acrylate, 2-hydroxy-3-butoxypropyl(meth)acrylate, tetrahydrofurfuryl(meth)acrylate, caprolactonedegeneration tetrahydrofurfuryl(meth)acrylate,2-ethyl-2-methyl-1,3-dioxolane-4-yl)methyl(meth)acrylate,(2-isobutyl-2-methyl-1,3-dioxolane-4-yl)methyl(meth)acrylate,(1,4-dioxaspiro[4,5]decane-2-yl)methyl(meth)acrylate,glycidyl(meth)acrylate, 3,4-epoxy cyclohexyl methyl(meth)acrylate,(3-ethyloxetane-3-yl)methyl(meth)acrylate, 2-(meth)acryloyloxymethylisocyanate, allyl(meth)acrylate, N-(meth)acryloyloxyethylhexahydrophthalimide, N-(meth)acryloyloxyethyl tetrahydro phthalimide,2-(meth)acryloyloxyethyl hexahydro phthalic acid,2-(meth)acryloyloxyethyl oxyethyl succinic acid, co-carboxypolycaprolactone mono(meth)acrylate, 2-(meth)acrylate oxyethyl acidphosphate, and the like.

Also, concrete examples of (meth)acrylic amides may include(meth)acrylamide, N,N-dimethyl(meth)acrylamide, N,N-diethyl(meth)acrylamide, N-methylol(meth)acrylamide,N-(3-N,N-dimethylaminopropyl)(meth)acrylamide,methylenebis(meth)acrylamide, ethylenebis(meth)acrylamide,N,N-diallyl(meth)acrylamide, and the like.

Also, concrete examples of maleimides may include N-methyl maleimide,N-hydroxyethyl maleimide, N-hydroxyethylcitraconimide, urethane acrylateof N-hydroxyethylcitraconimde and isophorone diisocyanate, and the like.

Concrete examples of (meth)acrylates having two (meth)acryloyl groups ina molecule may include 1,3-butanedioldi(meth)acrylate, 1,6-hexanedioldi(meth)acrylate, 1,9-nonanedioldi(meth)acrylate,1,10-decanedioldi(meth)acrylate, 1,3-butyleneglycoldi(meth)acrylate,2-methacryloyloxyethyl acid phosphate, ethyleneglycoldi(meth)acrylate,diethyleneglycoldi(meth)acrylate, triethyleneglycoldi(meth)acrylate,neopentylglycoldi(meth)acrylate, dipropyleneglycoldi(meth)acrylate,tripropyleneglycoldi(meth)acrylate, tetraethyleneglycoldi(meth)acrylate,cyclohexanedimethanoldi(meth)acrylate,polyethyleneglycoldi(meth)acrylate,polyethyleneglycol(200)di(meth)acrylate,polyethyleneglycol(400)di(meth)acrylate,polyethyleneglycol(600)di(meth)acrylate, glycerindi(meth)acrylate,2-hydroxy-3-acryloyloxypropylmethacrylate,dimethyloltricyclodecanedi(meth)acrylate, and the like.

Concrete examples of (meth)acrylates having three (meth)acryloyl groupsin a molecule may include trimethylolpropane tri(meth)acrylate,trimethylolpropane tri(meth)acrylate, trimethylolpropanetri(meth)acrylate, ditrimethylolpropane tri(meth)acrylate,trimethylolpropane tri(meth)acrylate, tri(2-hydroxy ethyl)isocyanuratetriacrylate, tri(2-hydroxy ethyl)isocyanurate, pentarythritoltriacrylate, ethoxylate trimethylolpropane tri(meth)acrylate,proxylatetrimethylolpropane tri(meth)acrylate, and the like.

Concrete examples of (meth)acrylates having four or five (meth)acryloylgroups in a molecule may include pentarythritol tetra(meth)acrylate, ditrimethylolpropane tetra(meth)acrylate, dipentarythritolpenta(meth)acrylate, epoxylate pentarythrotol tetra(meth)acrylate,pentaacrylate ester, and the like.

Concrete examples of (meth)acrylates having six (meth)acryloyl groups ina molecule may include dipentarythritol hexa(meth)acrylate.

The amount of the radical polymerization monomer is 0 parts by weight to40 parts by weight with respect to 100 parts by weight of the overalladhesive composition, preferably 5 parts by weight to 30 parts byweight, more preferably 5 parts by weight to 25 parts by weight.

Meanwhile, in case the adhesive composition includes radicalpolymerization monomers as above, it is preferable to mix aphoto-radical polymerization initiator in order to promote the radicalpolymerization and thus enhance the curing speed. Examples of thephoto-radical polymerization initiator may include, but are not limitedto, an acetonephenone-based photopolymerization initiator, a benzoinether-based photopolymerization initiator, a benzo phenone-basedphotopolymerization initiator, thioxanthone-based photopolymerizationinitiator, and the like. The amount of the photo-radical polymerizationinitiator is 0.5 parts by weight to 20 parts by weight with respect to100 parts by weight of the overall adhesive composition, preferably 0.5parts by weight to 15 parts by weight, more preferably 0.5 parts byweight to 10 parts by weight.

The cationic adhesive composition may further include a photo enhancer,an antioxidant, oligomer, and an adhesive promoter if necessary, andpreferably, may further include urethane acrylate in a weight ratio ofmore than 0 and not more than 4 parts by weight. In case urethaneacrylate is added as above, there is an increase in viscosity, but theviscosity of the adhesive may be lowered by elevating temperature.Meanwhile, in the case that urethane acrylate is added as above, it ispossible to provide more proper adhesive force in the use of theadhesive composition for acrylic films.

Since the foregoing adhesive composition of the present invention has alow amount of viscosity ranging from 15 cP to 50 cP, it exhibitssuperior workability and superior adhesive force in the case of thinadhesive layers.

Also, since the adhesive composition of the present invention has aglass transition temperature of not less than 90° C. after curing, ithas superior heat resistance. When heat resistant durability and thermalimpact was evaluated at 80° C., it was exhibited that in the case of apolarizer which was manufactured by using the adhesive composition ofthe present invention, breakage of the polarizing film did not occur.

Also, when the polarizer which was manufactured by using the adhesivecomposition of the present invention was immersed in water of 60° C. for24 hours, decoloration of the polarizing film was less than 10 mm in theMD direction, resulting in superior water resistance.

Thus, since the cationic adhesive has superior adhesive force andsuperior water resistance and heat resistance, it enables themanufacturing of a polarizer having superior characteristics.

Meanwhile, the double-sided polarizer of the present invention mayfurther include a primer layer at least between the first adhesive layerand the first transparent film or between the second adhesive layer andthe second transparent film.

The primer layer is to enhance the adhesive force of the transparentfilms and the adhesive layers, and is preferably formed of a primercomposition including a urethane polymer. For example, the primercomposition includes a urethane polymer, water-dispersible fineparticles, and water, more specifically, 1 part by weight to 50 parts byweight with respect to 100 parts by weight of the primer composition ofa urethane polymer, 0.1 parts by weight to 10 parts by weight ofwater-dispersible fine particles, and the balance of water.

The urethane polymer is obtained by reacting polyol and polyisocyanate.The polyol is not particularly limited if it has two or more hydroxylgroups, and any proper polyol may be employed. For example, the polyolmay be polyesterpolyol, polyether polyol, polycarbonatediol, or thelike, and polyesterpolyol, polyether polyol, and polycarbonatediol maybe used alone or in combinations thereof.

Preferably, the polyol may be at least one selected from the groupconsisting of ethylene glycol, 1,2-propaneondiol, 1,3-propanediol,1,3-butanediol, 1,4-butanediol, neolpentylglycol, pentanediol,1,6-hexanediol, 1,8-octanediol, 1,10-decanediol,4,4′-dihydroxyphenylpropane, 4,4′-dihydroxymethylmethane,diethyleneglycol, triethyleneglycol, polyethyleneglycol,dipropyleneglycol, polypropyleneglycol, 1,4-cyclohexanedimethanol,1,4-cyclohexanediol, bisphenol A, bisphenol F, glycerine,1,1,1-trimethylolpropane, 1,2,5-hexatriol, pentaerythriol, glucose,sucrose, and sorbitol.

Meanwhile, the polyesterpolyol may be representatively obtained byreacting a polybasic acid component and a polyol component. Examples ofthe polybasic acid component may include aromatic dicarboxylic acids,such as ortho-phthalic acid, isophthalic acid, terephthalic acid,1,4-naphthalene dicarboxylic acid, 2,5-naphthalene dicarboxylic acid,2,6-naphthalene dicarboxylic acid, biphenyl dicarboxylic acid,tetrahydrophthalic acid, and the like; aliphatic dicarboxylic acids,such as oxalic acid, succinic acid, malonic acid, glutaric acid, adipicacid, pimelic acid, suberic acid, azelaic acid, sebacic acid, linoleicacid, maleic acid, fumaric acid, mesaconic acid, itaconic acid; and thelike; alicyclic dicarboxylic acids, such as hexa-hydro phthalic acid,tetrahydro phthalic acid, 1,3-cyclohexane dicarboxylic acid,1,4-cyclohexane dicarboxylic acid, and the like; and reactivederivatives, such as acid anhydrides thereof, alkyl ester, acid halide.The above polybasic acid components may be used alone or in combinationsthereof. Further, it is more preferable that the polybasic acidcomponent is at least one selected from the group consisting ofpolytetramethyleneglycol (PTMG), polypropyleneglycol (PPG), andpolyethyleneglycol (PEG).

It is preferable that the polycarbonatepolyol is at least one selectedfrom the group consisting of poly(hexamethylene carbonate)glycol andpoly(cyclohexanecarbonate)glycol.

The polyether polyol may be obtained by ring-opening polymerization ofalkyleneoxide to a polyalcohol. Examples of the polyalcohol may includeethyleneglycol, diethyleneglycol, propyleneglycol, dipropyleneglycol,glycerin, trimethylolpropane, and the like. The foregoing polyalcoholsmay be used alone or in combinations thereof.

The isocyanate is not limited if it is a compound having two or more NCOgroups, and may include, for example, toluene diisocyanate (TDI),4,4-diphenyl methane diisocyanate (MDI), 1,5-naphthalene diisocyanate(NDI), tolidine diisocyanate (TODI), hexamethylene diisocyanate (HMDI),isophorone diisocyanate (IPDI), p-phenylene diisocyanate,transcyclohexane, 1,4-diisocyanate, and xylene diisocyanate (XDI). Theseisocyantes may be used alone or in combinations thereof.

A preparation method of the urethane resin may employ any proper methodknown in the art. Concrete example of the known method may include a oneshot method of reacting respective components once, and a multi-stagemethod reacting respective components in stages. In the case that theurethane resin has a carboxylic group, the urethane resin is preferablyprepared by the multi-stage method because the multi-stage method mayeasily introduce the carboxylic group. Further, while the urethane resinis prepared, any proper urethane reaction catalyst may be used.

In the preparation of the urethane resin, another polyol and/or anotherchain extender may be added for a reaction in addition to the abovecomponents.

Examples of another polyol may include polyols having three or morehydroxyl groups, such as sorbitol, glycerin, trimethylolethane,trimethylolpropane, pentaerythritol, and the like.

Examples of a chain extender may include glycols, such asethyleneglycol, diethylene glycol, triethylene glycol, 1,3-propanediol,1,3-butanediol, 1,4-butanediol, neopentyl glycol, pentane diol,1,6-hexane diol, propylene glycol, and the like; aliphatic diamines,such as ethylene diamine, propylene diamine, hexamethylene diamine,1,4-butane diamine, aminoethyl alkanolamine, and the like; alicyclicdiamines, such as isophorone diamine, 4,4′-dicyclohexylmethane diamine,and the like; and aromatic diamines, such as xylylene diamine, tolylenediamine, and the like.

Further, while the urethane resin is prepared, a neutralizer may beused. The use of the neutralizer may enhance the stability of theurethane resin in water. Examples of the neutralizer may include, forexample, N-methylmorpho line, triethylamine, dimethylethanolamine,methyldiethanolamine, triethanolaminealkyne, morpholine, tripropylamine,ethanolamine, triisopropanolamine, and the like. The foregoingneutralizers may be used alone or in combinations thereof.

In preparing the urethane resin, an organic solvent, inactive withrespect to the polyisocyanate and miscible with water is used. Examplesof the organic solvent may include ester-based solvents, such as ethylacetate, ethylcellosolve acetate, and the like; ketone-based solvents,such as acetone, methylethylketone, methylisobutylketone, and the like;ether-based solvents, such as dioxane, tetrahydrofuran, and the like.The foregoing organic solvents may be used alone or in combinationsthereof.

Meanwhile, it is more preferable that the urethane polymer includes acarboxylic group. The reason the urethane polymer includes a carboxylicgroup is because water dispersibility is enhanced to thus furtherenhance the adhesion between the adhesive layer and the transparentfilm.

The urethane polymer including the carboxylic group may be obtained, forexample, by reacting a chain extender with polyol and polyisocyanate.Examples of the chain extender having the carboxylic group may includedihydroxy carboxylic acid, dihydroxy succinate, and the like. Examplesof the dihydroxy carboxylic acid may include dialylol alkanic acidsincluding dimethylolalkanic acid, such as dimethylolacetic acid,dimethyolbutanoic acid, dimethylol propionic acid, dimethyolbutyricacid, dimethylol pentanoic acid, or the like. The above-describedpolybasic acid components may be used alone or in combinations thereof.

Meanwhile, the amount of the urethane polymer is preferably about 1 partby weight to about 50 parts by weight with respect to 100 parts byweight of the primer composition, more preferably about 3 parts byweight to about 20 parts by weight, most preferably 5 parts by weight to15 parts by weight. If the urethane polymer is contained in a weightratio less than 1 part by weight, the adhesiveness is lowered, and ifthe urethane polymer is contained in a weight ratio more than 30 partsby weight, the viscosity is increased, so that a leveling may be notachieved and a dying time may be increased.

The weight average molecular weight of the urethane polymer ispreferably 10,000 to 100,000. If the weight average molecular weight isless than 10,000, the adhesive force is lowered, and if the weightaverage molecular weight exceeds 100,000, it is difficult to prepare awater-dispersible urethane.

The water-dispersible fine particles that are usable in the presentinvention may be any proper fine particles, preferably water-dispersiblefine particles. Specifically, both inorganic fine particles and organicfine particles may be used. Examples of the inorganic fine particles mayinclude inorganic oxide particles, such as silica, titania, alumina,zirconia, antimony oxides, and the like. Examples of the organic fineparticles may include silicon resins, fluorine resins, (meth)acrylicresins, cross-linked polyvinyl alcohols, melamine resins, and the like.

Among the water-dispersible fine particles, silica is preferably used.The reason silica is used is because silica is superior in blockinginhibition and transparency not to generate hazing, and is free ofcolorization to have a low amount of influence on the optical propertiesof the polarizer. Also, since silica is good in terms of dispersibilityand dispersion stability with respect to primer compositions, theworkability for forming the primer layer is more superior than othermaterials.

The average diameter (average primary particle diameter) of thewater-dispersible fine particles is preferably 10 nm to 200 nm, morepreferably 20 nm to 70 nm. When the average diameter of thewater-dispersible fine particles is less than 10 nm, surface energy isincreased, so that agglomeration and precipitation of silica in a primersolution occurs to thereby cause a problem in stability of the solution.When the average diameter is more than 200 nm, silica particles are notuniformly dispersed in the solution and are agglomerated, so that thesize of silica is increased to be larger than the wavelength band(400-800 nm) of visible light, and thus silica scatters light of notless than 400 nm to increase hazing. By using the fine particles havingthe foregoing diameter range, irregularities may be properly formed atthe surface of the primer layer to effectively reduce frictional forcein a contact surface between an acrylic-based film and the primer layerand/or between the primer layers. As a result, blocking inhibition maybe further enhanced.

It is preferable that the amount of the water-dispersible fine particlesis 0.1 parts by weight to 10 parts by weight with respect to 100 partsby weight of the primer composition. If the amount of thewater-dispersible is less than 0.1 parts by weight, slippage betweenfilms on winding does not occur, so that film tearing may occur. If theamount of the water-dispersibility exceeds 10 parts by weight, hazingmay occur.

Since the primer composition of the present invention is aqueous, thefine particles are preferably mixed in an aqueous disperson form.Specifically, in case silica is employed as fine particles, silica ispreferably mixed in a colloidal silica form. As the colloidal silica,products commercially available in the art may be used, and for example,Snowtex series from Nissan chemical, AEROSIL series from Air product,Epostar series from Nippon catalyst, and Soliostar RA series, LSH seriesfrom Ranco, and the like may be used.

Meanwhile, the primer composition may further include a cross-linkingagent if necessary. Methylol compounds, such as oxazolin, boric acid,trimethylolmelamine, and the like, carbodiimide, isocyanate, azyridinecompounds, and the like may be used as the cross-linking agent.

The cross-linking agent is preferably contained in an amount of 0.1parts by weight to 30 parts by weight with respect to 100 parts byweight of the primer composition. In case a primer containing thecross-linking agent is used, since the primer layer prevents water frompenetrating, the primer composition exhibits superior opticalproperties, such as water resistance and moisture and heat resistance.

Also, the primer composition may further include a silane couplingagent, a fluorine surfactant, a silane surfactant, and a surfactantcontaining an alkyl group as other additives if necessary.

The primer layer formed of the above primer composition is preferablyabout 100 nm to about 1 μm thick. If the primer layer is not more than100 nm, the adhesive force is decreased, and if the primer layer is notless than 1 μm, the primer layer coated is not completely dried and thusblocking between films may occur, resulting in a tearing of the films.

Also, it is preferable that a water contact angle of a surface of theprimer layer is 40 degrees to 100 degrees, more preferably 50 degrees to90 degrees, most preferably 60 degrees to 80 degrees. If the watercontact angle is less than 40 degrees, the hydrophilicity of the primerlayer is increased and thus the primer layer reacts with iodine in thepolarizing film to inhibit an arrangement of iodine, thus scattering asingle body color and deteriorating the degree of polarization. If thewater contact angle exceeds 100 degrees, the hydrophobicity of theprimer layer is increased and thus adhesion between the primer layer andthe polarizing film becomes difficult.

Next, the first transparent film and the second transparent film arepolarizing film protecting films or compensation films for compensatingfor light characteristics of the polarizing film, and may includepolymer films known to the art. The first transparent film and thesecond transparent film may be formed of the same material or differentmaterials.

More specifically, the transparent film may be at least one selected,but is not limited thereto, from the group consisting of, for example,an acrylic film, a PEF film, an acrylic-based primer-treated PET film, apolynorbornene (PNB) film, a COP film, a polycarbonate film and TACfilms including NRT (Fuji film), N TAC (Konica), V TAC (Fuji film), UZTAC (Fuji film), and the like. Among the foregoing films, the acrylicfilm is particularly preferable.

In the present invention, the acrylic film used as the transparent filmmay contain a (meth)acrylate resin. The film containing the(meth)acrylate resin may be obtained, for example, by extruding aforming material containing the (meth)acrylate resin as a maincomponent.

The acrylic film may be a film including a copolymer having analkyl(meth)acrylate unit and a styrene unit, and an aromatic resinhaving a carbonate group at a main chain thereof, or a film including analkyl(meth)acrylate unit, a styrene unit, 3 to 6-membered heterocyclicunit substituted with at least one carbonyl group, and a vinyl cyanideunit.

The acrylic film may be a film including a (meth)acrylate resin having aaromatic ring. An example of the (meth)acrylate resin having thearomatic ring is a resin composition described in Korean Patent LaidOpen Publication No. 10-2009-0115040 and including (a) a (meth)acrylateunit including one or more (meth)acrylate derivative; (b) an aromaticunit having a chain with a hydroxy group-contained part, and an aromaticpart; and (c) a styrene unit including one or more styrene derivative.Units (a) to (c) may be contained in a resin composition in a copolymerform, or at least two of units (a) to (c) may be contained in a resincomposition in a copolymer form.

The acrylic film may be a film including an acrylic resin having alactone ring structure. Concrete examples of the (meth)acrylate resinhaving the lactone ring structure are described in Japanese PatentApplication Laid Open Publication No. 2000-230016, Japanese PatentApplication Laid Open Publication No. 2001-151814, Japanese PatentApplication Laid Open Publication No. 2002-120326, etc.

A method of preparing the acrylic film is not particularly limited. Forexample, the acrylic film may be prepared by sufficiently mixing a(meth)acrylate resin, a polymer, and additives by any proper mixingmethod to form a thermoplastic resin composition, and then forming afilm from the thermoplastic resin composition, or by preparing a(meth)acrylate resin, a polymer, and additives in respective separatesolutions, mixing the solutions to form a uniform mixing solution, andthen forming a film from the mixing solution.

The thermoplastic resin composition is prepared, for example, bypreblending the film raw materials by using any proper mixer, such as anomni mixer to obtain a mixture and then extruding and mulling theobtained mixture. In this case, the mixer used in the extruding andmulling is not particularly limited, and any proper mixer, such as asingle-screw extruder, a double-screw extruder, a dispersion kneader, orthe like may be used.

The method of forming a film may include any proper forming methods,such as, a solution casting method (solution emulsifying method), a meltextrusion method, a calendar method, a compressive molding method. Amongthe foregoing film forming methods, the solution casting method(solution emulsifying method) and the melt extrusion method arepreferable.

Examples of a solvent used in the solution casting method (solutionemulsifying method) may include: aromatic hydrocarbons such as benzene,toluene, xylene, and the like; aliphatic hydrocarbons such ascyclohexane, decalin, and the like; esters such as ethyl acetate, butylacetate; ketones such as acetone, methyl ethyl ketone, methyl isobutylketone, and the like; alcohols such as methanol, ethanol, isopropanol,butanol, isobutanol, methyl cellosolve, ethyl cellosolve, butylcellosolve, and the like; ethers such as tetrahydrofuran, dioxane, andthe like; halogenated hydrocarbons such as dichloromethane, chloroform,carbon tetrachloride, and the like; dimethylformamide; dimethylsulfoxide, and the like. These solvents may be used or in combinationsthereof.

Examples of an apparatus for performing the solution casting method(solution emulsifying method) may include a drum type casting machine, aband type casting machine, a spin coater, and the like. Examples of themelt extrusion method may include a T-die method, an inflation method,and the like. The forming temperature is preferably 150-350° C., andmore preferably 200-300° C.

In case the film is formed by using the T-die method, a T-die isinstalled at a front edge of a single-screw extruder or double-screwextruder published, and the extruded film is wound to obtain aroll-shaped film. At this time, by properly adjusting the temperature ofthe winding roll to apply an elongation in an extruding direction, thefilm may be uniaxially elongated. By elongating the film in a directionperpendicular to the extrusion direction, a simultaneous biaxialelongation or a sequential biaxial elongation may be performed.

The acrylic film may be any of a non-elongated film or an elongatedfilm. In the case of the elongated film, the elongated film may be auniaxial elongation film or a biaxial elongation film, and in the caseof the biaxial elongation film, the biaxial elongation film may be anyof a simultaneous biaxial elongation film or a sequential biaxialelongation film. The biaxial elongation enhances the mechanical strengthof the film to thus enhance the film performance. In case the acrylicfilm mixed with another thermoplastic resin is elongated, the acrylicfilm may suppress an increase in phase difference and maintain theoptical isotropy.

The elongation temperature is preferably in a range near the glasstransition temperature of the thermoplastic resin composition that is afilm raw material, for example, (glass transition temperature −30° C.)to (glass transition temperature +100° C.), more preferably, (glasstransition temperature −20° C.) to (glass transition temperature +80°C.). If the elongation temperature is less than (glass transitiontemperature −30° C.), a sufficient extension magnification may not beobtained. On the contrary, if the elongation temperature exceeds (glasstransition temperature +100° C.), the flow of the resin composition mayoccur to hinder a stable elongation.

The elongation magnification defined by an area ratio is 1.1 to 25times, more preferably 1.3 to 10 times. If the elongation magnificationis less than 1.1 times, an enhancement in toughness following theelongation may not be obtained. If the elongation magnification exceeds25 times, an effect according to an increase in elongation magnificationmay be insufficient.

The elongation speed in one direction is preferably 10-20,000%/min, morepreferably 100-10,000%/min. If the elongation speed is less than10%/min, an extended period of time may be required to obtain asufficient elongation magnification to elevate the preparation costs. Ifthe elongation speed exceeds 20,000%/min, a tearing of the elongatedfilm may occur.

The acrylic film may be thermally annealed after elongation, so as tostabilize the optical isotropy or mechanical characteristics thereof.The annealing condition is not particularly limited, and any propercondition known in the art may be employed.

Meanwhile, a surface treatment for enhancement of the adhesive force maybe performed with respect to the transparent films if necessary. Forexample, at least one surface treatment selected from the groupconsisting of an alkali treatment, a corona treatment, and a plasmatreatment.

The foregoing polarizer according to the present invention may beprepared, for example, by coating a primer composition on one surface ofa transparent film to form a primer layer, coating an adhesivecomposition on one surface of the primer layer or a polarizing film toform an adhesive layer, attaching the polarizing film and thetransparent film, and curing the adhesive composition through a lightirradiation.

The polarizer according to the present invention may be usefully appliedto optical devices, such as liquid crystal displays, etc. For example,the optical device of the present invention may be a liquid crystalpanel or a liquid crystal display including such a liquid crystal paneland polarizers disposed on both surfaces of the liquid crystal panel. Atthis time, one of the polarizers may be a polarizer according to thepresent invention. At this time, the type of the liquid crystal panelincluded in the liquid crystal display is not particularly limited. Forexample, published panels, for example, passive matrix panels, such as atwisted nematic (TN) type, a super twisted nematic (STN) type, aferroelectric (F) type, or a polymer dispersed (PD) type; active matrixpanels such as a two terminal type, or a three terminal type; an inplane switching (IPS) panel; and a vertical alignment (VA) panel may beall applied regardless of the type. Also, types of other elementsconstituting the liquid crystal display, for example, upper and lowersubstrates (i.e., color filter substrate and array substrate) are notparticularly limited, and elements published in the art may be employedwithout any limitation.

MODE FOR INVENTION

Hereinafter, the present invention will be described in more detail withexamples thereof. However, following examples are merely provided forillustration, and the scope of the present invention is not limited tothe following examples.

Preparation Example 1 Preparation of Transparent Film

A resin composition, in whichpoly(N-cyclohexylmaleimide-co-methylmethacrylate) resin, styrene-maleicanhydride copolymer resin and phenoxy resin were uniformly mixed in aweight ratio of 100:2.5:5, was supplied to a 24φ-extruder that wassubstituted with nitrogen from a raw material hopper to the extruder,and melted at 250° C. to obtain raw material pellets.

As the phenoxy based resin, PKFE (Mw=60,000, Mn=16,000, T.sub.g=98° C.)manufactured by InChemRez® Co., Ltd., was used; as the styrene-maleicanhydride copolymer resin, Dylaeck 332 containing 85 wt % of styrene and15 wt % of maleic anhydride was used; and thepoly(N-cyclohexylmaleimide-co-methylmethacrylate) resin in which thecontent of N-cyclohexylmaleimide measured by NMR analysis is 6.5 wt %was used.

The obtained raw material pellets were dried under a vacuum, melted at260° C. by using the extruder and passed through a coat hanger typedT-die, and then passed through the chrome coated casting roll and thedrying roll to thereby prepare a film having a thickness of 150 μm. Thisfilm was elongated by a ratio of 170% using a difference in speedbetween rolls in an MD direction at 125° C. by using a pilot elongatingapparatus.

(1) Preparation of Acrylic Film A

An acrylic film prepared through the process above was subjected tocorona treatment, and one side of the acrylic film was then coated, byusing a #7 bar, with a primer composition, in which 10 parts by weightof carbodiimide-based cross-linking agent (carbodinite SV-02manufactured by Nisshinbo Chemical) was added to a primer compositionhaving 10 wt % of a solid component which was prepared by dilutingCK-PUD-F (Chokwang urethane dispersion) with pure water. Thereafter, theprimer composition was elongated at 130° C. in a TD direction by 190%using a tenter to obtain an acrylic film A having a primer layerthickness of 400 nm.

(2) Preparation of Acrylic Film B

The acrylic film prepared according to (1) of Preparation Example 1 wassubjected to a corona treatment, and one side of the acrylic film wasthen coated, by using a #7 bar, with a primer composition, in which 20parts by weight of oxazoline cross-linking agent (WS700 manufactured byNippon Shokubai Co., Ltd.) was added to a primer composition having 10wt % of a solid component which was prepared by diluting CK-PUD-F(Chokwang urethane dispersion) with pure water. Thereafter, the primercomposition was elongated at 130° C. in a TD direction by 190% using atenter to obtain an acrylic film B having a primer layer thickness of400 nm.

Preparation Example 2 Preparation of Adhesive Composition

(1) Adhesive Composition A

5 parts by weight of CPI 100P (Sanapro) as a cationic initiator wasadded to 100 parts by weight of a resin composition which was obtainedby adding 25 wt % of3,4-epoxycyclohexylmethyl-3,4′-epoxycyclohexanecarboxylate (Celloxide2021P of Dicel Chemical Industries, Ltd), 25 wt % of 1,4-cyclohexanedimethanol diglycidylether, 35 wt % of3-ethyl-3-[(3-ethyloxetane-3-yl)methoxymethyl]oxetane (Aron Oxcetane DOX221, Toagosei Co., Ltd.), and 15 wt % of 3-ethyl-3-hydroxymethyl oxetane(Aron Oxcetane OXA, Toagosei Co., Ltd.), thus preparing an adhesivecomposition A for a polarizer.

(2) Adhesive Composition B

5 parts by weight of CPI 100P (Sanapro) as a cationic initiator and 5parts by weight of vinyl triethoxysilane were added to 100 parts byweight of a resin composition which was obtained by adding 25 wt % of3,4-epoxycyclohexylmethyl-3,4′-epoxycyclohexanecarboxylate (Celloxide2021P of Dicel Chemical Industries, Ltd), 25 wt % of 1,4-cyclohexanedimethanol diglycidylether, and 50 wt % of3-ethyl-3-[(3-ethyloxetane-3-yl)methoxymethyl]oxetane (Aron Oxcetane DOX221, Toagosei Co., Ltd.), thus preparing an adhesive composition B for apolarizer.

(3) Adhesive Composition C

5 parts by weight of CPI 100P (Sanapro) as a cationic initiator and 5parts by weight of vinyl acetate were added to 100 parts by weight of aresin composition which was obtained by adding 25 wt % of3,4-epoxycyclohexylmethyl-3,4′-epoxycyclohexanecarboxylate (Celloxide2021P of Dicel Chemical Industries, Ltd), 25 wt % of 1,4-cyclohexanedimethanol diglycidylether, and 50 wt % of3-ethyl-3-[(3-ethyloxetane-3-yl)methoxymethyl]oxetane (Aron Oxcetane DOX221, Toagosei Co., Ltd.), thus preparing an adhesive composition C for apolarizer.

Example 1

By using a micro gravure coater, primer layers of 2 sheets of theacrylic film A prepared by Preparation Example 1 were coated withadhesive composition A such that a final thickness of the adhesive layerwas 1 μm. Thereafter, the two sheets of the acrylic film (A) coated withthe adhesive composition was laminated on both sides of a PVA device,and ultraviolet (UV) light of 500 mJ/cm² was irradiated in a one-sidedirection of the PVA device using a UV irradiation apparatus (forexample, metal halide lamp) to obtain a polarizer.

Example 2

A polarizer was prepared in the same manner as Example 1 except thatadhesive composition B was used.

Example 3

A polarizer was prepared in the same manner as Example 1 except thatadhesive composition C was used.

Example 4

A polarizer was prepared in the same manner as Example 1 except that theadhesive composition was coated to have a thickness of 3 μm.

Example 5

A polarizer was prepared in the same manner as Example 2 except that theadhesive composition was coated to have a thickness of 3 μm.

Example 6

A polarizer was prepared in the same manner as Example 3 except that theadhesive composition was coated to have a thickness of 3 μm.

Example 7

The primer layers of the acrylic film A prepared by Preparation Example1 was coated with adhesive composition A using a micro gravure coatersuch that a final thickness of the adhesive layer was 1 μm (hereinafter,referred to as ‘acrylic film A-1’). Also, the primer layers of theacrylic film A prepared by Preparation Example 1 was coated withadhesive composition A using a micro gravure coater such that a finalthickness of the adhesive layer was 3 μm (hereinafter, referred to as‘acrylic film A-2’). Thereafter, the acrylic film A-1 and the acrylicfilm A-2 were laminated on both sides of a PVA device, and UV light of500 mJ/cm² was irradiated onto a side on which the acrylic film A-2 waslaminated using a UV irradiation apparatus (for example, metal halidelamp) to obtain a polarizer.

Example 8

The primer layers of the acrylic film A prepared by Preparation Example1 was coated with adhesive composition A using a micro gravure coatersuch that a final thickness of the adhesive layer was 3 μm (hereinafter,referred to as ‘acrylic film A-3’). Also, the primer layers of acrylicfilm A prepared by Preparation Example 1 were coated with adhesivecomposition A using a micro gravure coater such that a final thicknessof the adhesive layer was 10 μm (hereinafter, referred to as ‘acrylicfilm A-4’). Thereafter, acrylic film A-3 and the acrylic film A-4 werelaminated on both sides of a PVA device, and UV light of 500 mJ/cm² wasirradiated onto a side on which the acrylic film A-4 was laminated usinga UV irradiation apparatus (for example, metal halide lamp) to obtain apolarizer.

Example 9

The primer layers of the acrylic film B prepared by Preparation Example1 was coated with adhesive composition A using a micro gravure coatersuch that a final thickness of the adhesive layer was 1 μm (hereinafter,referred to as ‘acrylic film B-1’). Also, the primer layers of theacrylic film B prepared by Preparation Example 1 were coated withadhesive composition A using a micro gravure coater such that a finalthickness of the adhesive layer was 3 μm (hereinafter, referred to as‘acrylic film B-2’). Thereafter, the acrylic film B-1 and the acrylicfilm B-2 were laminated on both sides of a PVA device, and UV light of500 mJ/cm² was irradiated onto a side on which the acrylic film B-2 waslaminated using a UV irradiation apparatus (for example, metal halidelamp) to obtain a polarizer.

Comparative Example 1

A polarizer was prepared in the same manner as Example 1 except that theadhesive composition was coated to a thickness of 5 μm.

Comparative Example 2

A polarizer was prepared in the same manner as Example 2 except that theadhesive composition was coated to a thickness of 5 μm.

Comparative Example 3

A polarizer was prepared in the same manner as Example 3 except that theadhesive composition was coated to a thickness of 5 μm.

Experimental Example 1 Evaluation of Delamination Force of Polarizer

Measurement for delamination force of a first adhesive layer wasperformed on the polarizers prepared by Examples 1 to 9 and ComparativeExamples 1 to 3. The delamination force was obtained by measuring adelamination force when the acrylic film on a side where UV light wasnot irradiated was delaminated from the PVA device by using a polarizerhaving a width of 20 mm and a length of 100 mm. The results are shown inTable 1 below. The case where the delamination force exceeds 2 N/cm wasrepresented as OK, and otherwise as NG.

Experimental Example 2 Evaluation of Water Resistance

The polarizers prepared by Examples 1 to 9 and Comparative Examples 1 to3 were laminated on a glass substrate, and then immersed in a constanttemperature bath of 60° C. Water resistance was determined by observingwhether an end of the polarizer after the elapse of 8 hours wasdecolored or not. The case where in which was no change was representedas OK, and otherwise as NG.

Experimental Example 3 Evaluation of Thermal Impact Property

The polarizers prepared by Examples 1 to 9 and Comparative Examples 1 to3 were laminated on a glass substrate, and then left for 30 minutes at−40° C. Thereafter, the polarizers are left for 30 minutes at 80° C.again and this was repeated 100 times. Afterwards, whether the externalappearance of the polarizer was deformed was estimated with the nakedeye. The case where the external appearance of the polarizer was notdeformed was represented as OK, and otherwise as NG. The results areshown in Table 2 below.

TABLE 2 Thickness Thickness Delamination Primer of first of second forceof Surface Surface not adhesive adhesive first irradiated irradiatedlayer layer adhesive Water Thermal Item with UV with UV Adhesive [μm][μm] layer resistance impact Example 1 10 parts by 10 parts by A 1 1 OKOK OK weight of weight of CkPUD F + SV-02 CkPUD F + SV-02 Example 2 10parts by 10 parts by B 1 1 OK OK OK weight of weight of CkPUD F + SV-02CkPUD F + SV-02 Example 3 10 parts by 10 parts by C 1 1 OK OK OK weightof weight of CkPUD F + SV-02 CkPUD F + SV-02 Example 4 10 parts by 10parts by A 3 3 OK OK OK weight of weight of CkPUD F + SV-02 CkPUD F +SV-02 Example 5 10 parts by 10 parts by B 3 3 OK OK OK weight of weightof CkPUD F + SV-02 CkPUD F + SV-02 Example 6 10 parts by 10 parts by C 33 OK OK OK weight of weight of CkPUD F + SV-02 CkPUD F + SV-02 Example 710 parts by 10 parts by A 1 3 OK OK OK weight of weight of CkPUD F +SV-02 CkPUD F + SV-02 Example 8 10 parts by 10 parts by A 3 10 OK OK OKweight of weight of CkPUD F + SV-02 CkPUD F + SV-02 Example 9 20 partsby 20 parts by A 1 3 OK OK OK weight of weight of CkPUD F + WS700 CkPUDF + WS700 Comparative 10 parts by 10 parts by A 5 5 NG OK OK Example 1weight of weight of PUD CkPUD F + SV-02 F + SV-02 Comparative 10 partsby 10 parts by B 5 5 NG OK OK Example 2 weight of weight of PUD CkPUDF + SV-02 F + SV-02 Comparative 10 parts by 10 parts by C 5 5 NG OK OKExample 3 weight of weight of PUD CkPUD F + SV-02 F + SV-02

1. A double-sided polarizer comprising: a polarizing film; a firstadhesive layer formed on one surface of the polarizing film; a secondadhesive layer formed on the other surface of the polarizing film; afirst transparent film formed on the first adhesive layer; and a secondtransparent film formed on the second adhesive layer, wherein the firstadhesive layer and the second adhesive layer are formed of an activeenergy line-curable adhesive, and the first adhesive layer is 0.1 μm to3 μm thick.
 2. The double-sided polarizer of claim 1, wherein the secondadhesive layer is 0.1 μm to 10 μm thick.
 3. (canceled)
 4. Thedouble-sided polarizer of claim 1, wherein the irradiating of the activeenergy line is performed through an active energy source positioned inthe direction of the transparent film formed on the second adhesivelayer.
 5. The double-sided polarizer of claim 1, wherein the firstadhesive layer and the second adhesive layer are formed of a cationicadhesive.
 6. The double-sided polarizer of claim 5, wherein the cationicadhesive include: (1) 5 wt % to 90 wt % of an epoxy compound having atleast two epoxy groups in a molecule; (2) 5 wt % to 90 wt % of anoxetane compound having at least one oxetanyl group in a molecule; and(3) 0.5 wt % to 20 wt % of a cationic photo-polymerization initiator. 7.The double-sided polarizer of claim 6, wherein the epoxy compound is acombination of a first epoxy compound including one or more epoxidizedaliphatic ring group, and a second epoxy compound including one or moreglycidyl ether group.
 8. The double-sided polarizer of claim 6, whereinthe cationic adhesive further comprises one or more selected from thegroup consisting of a silane coupling agent, a vinyl compound, and aradical polymerization monomer.
 9. The double-sided polarizer of claim1, further comprising a primer layer at least between the first adhesivelayer and the first transparent film or between the second adhesivelayer and the second transparent film.
 10. The double-sided polarizer ofclaim 9, wherein the primer layer is formed of a primer compositionincluding 1 part to weight to 50 parts by weight of a urethane polymer,0.1 part by weight to 10 parts by weight of a water-dispersed fineparticles, and the balance of water.
 11. The double-sided polarizer ofclaim 10, wherein the primer composition further comprises across-linking agent.
 12. The double-sided polarizer of claim 9, whereinthe primer layer is 100 nm to 1 μm thick.
 13. The double-sided polarizerof claim 1, wherein at least one of the first transparent film and thesecond transparent film is an acrylic film.
 14. An optical devicecomprising a double-sided polarizer of claim 1.